主要组成 Main composition | 以氯醚树脂为主，用丙烯酸改性树脂改性，将各种着色颜料分散在其中并加入各种助剂、有机溶剂等经研磨调制而成。 It is mainly made of chloroether resin and modified by acrylic acid modified resin, in which various coloring pigments are dispersed and various auxiliaries and organic solvents are added and prepared by grinding. |
主要特性Main characteristics | 该漆干性快，漆膜耐酸、耐碱、耐候性优异，同时该漆的光泽、机械性能均良好。 The paint has fast dryness, excellent acid resistance, alkali resistance and weather resistance. At the same time, it has good gloss and mechanical properties. |
主要用途Main use | 适用于室内外化工设备、钢架、桥梁、水泥墙面等易受酸碱盐腐蚀的表面保护及装饰。 It is suitable for surface protection and decoration of indoor and outdoor chemical equipment, steel frame, bridge, cement wall and so on, which are easily corroded by acid, alkali and salt. |
基本参数 Basic parameters | 干燥时间（25℃）：表干≤20min，实干≤24h Drying time (25 ℃): surface drying ≤ 20min, actual drying ≤ 24 hours. |
附着力（划格法）：≤1 级 Adhesion (grid method): ≤ 1 grade | |
配套用漆Matching paint | 环氧富锌底漆、无机富锌底漆、各色环氧防锈底漆。 Epoxy zinc-rich primer, inorganic zinc-rich primer, all kinds of epoxy antirust primer. |
复涂间隔时间Interval time of recoating | （25℃）24 小时，（30℃）16 小时，或视具体情况而定，不可超过7 天。 (25 ℃) 24 hours, (30 ℃) 16 hours, or as the case may be, not more than 7 days. |
表面处理Surface treatment | 工件表面要处理干净，如直接涂于钢材表面，钢材表面除锈等级要达到GB8623-88、SA2.5 以上或ST3 级，表面粗糙 30～70μm。 The surface of the workpiece should be cleaned, such as directly applied to the steel surface, the rust removal grade of the steel surface should reach GB8623-88, SA2.5 or ST3, and the surface is rough 30 ~ 70 μ m. |
建议施工道数Recommended numberof construction roads | 一般防护涂装要求一底两面或两底两面，底面复合涂层干膜总厚度≥125μm，要求不高时采用一底一面施工，底面复合涂层干膜总厚度≥70μm。 The general protective coating requires one bottom two sides or two bottom two sides, the total dry film thickness of the bottom composite coating is more than 125 μ m, when the requirement is not high, the construction of one bottom side is adopted, and the total dry film thickness of the bottom composite coating is ≥ 70 μ m. |
施工参考Construction reference | 以喷涂为主，也可淋涂、浸涂、滚涂、刷涂，使用前将漆液充分搅匀，并且不允许与其他不同性质、不同品种漆混合使用，该漆已喷涂为主，使用前必须将漆液搅拌均匀，如粘度过大，用配套稀释剂稀释，施工粘度一般以14～20 秒（涂-4 粘度计，25±1℃）为宜。 Mainly spray, can also spray, dip, roll, brush, stir the paint well before use, and is not allowed to be mixed with other different properties and different kinds of paint, the paint has been sprayed mainly, the paint must be stirred evenly before use, if the viscosity is too high, diluted with matching diluents, the construction viscosity is generally 14 seconds (coating-4 viscometer, 25 ±1 ℃). 如有粗颗粒或机械杂质应使用80 目以上滤网过滤后再喷涂，不能用汽油、松节油、醇类等单一溶剂稀释，否则会影响施工质量，甚至造成报废。 If there are coarse particles or mechanical impurities should be filtered with more than 80 mesh filter before spraying, can not be diluted with gasoline, turpentine, alcohols and other single solvent, otherwise it will affect the construction quality, or even lead to scrap. |
注意事项 Matters needing attention | 1、配漆和施工过程中，严禁与水、酸、碱等接触。 1. In the process of paint preparation and construction, contact with water, acid, alkali and so on is strictly prohibited. 2、施工及干燥过程环境相对湿度不得大于 85%。 2. The relative humidity of the environment in the construction and drying process shall not be greater than 85%. |
储藏期限 Storage period | 产品在规定储运条件下，漆料储存期为12 个月，超过储存期可按质量标准检验，如符合技术要求，仍可使用。Under the specified storage and transportation conditions, the storage period of paint is 12 months, which can be inspected according to the quality standard after the storage period. If it meets the technical requirements, it can still be used. |
附注：本说明书有关数据是在标准条件下实验取得，实际使用时，因环境条件和施工方法的差异可能与之略有不同，以上数据如有改变，已本厂最新说明书为准，恕不另行通知。 Note: the relevant data in this manual are obtained by experiment under standard conditions. In actual use, they may be slightly different due to differences in environmental conditions and construction methods. If the above data are changed, the latest instructions of our factory will prevail without prior notice. | |