主要组成 Main composition | 该漆是由干性植物油改性醇酸树脂，铁红粉等防锈颜料经研磨后，加入催干剂、有机溶剂等调制而成。 The paint is made of dry vegetable oil modified alkyd resin, iron red powder and other antirust pigments after grinding and adding driers and organic solvents. | |
主要特性Main characteristics | 漆膜具有良好的附着力和一定的防锈性能，与硝基、醇酸等面漆结合力好，在一般气候条件下耐久性好，但在湿热条件下耐久性较差。 The paint film has good adhesion and certain anti-rust performance, good adhesion with nitro, alkyd and other topcoats, good durability in general climate conditions, but poor durability in hot and humid conditions. | |
主要用途Main use | 该底漆适用于涂覆在黑色金属表面上，起打底防锈作用。 The primer is suitable for coating on the surface of ferrous metal and plays the role of priming and anti-rust. | |
基本参数 Basic parameters | 干燥时间（25℃） Drying time (25 ℃) | 表干≤20min Table dry ≤ 20min |
干燥时间（25℃） Drying time (25 ℃) | 实干≤36h Actual work ≤ 36H | |
烘干（105±2℃），h Drying (105 ±2 ℃), h | 0.5 | |
粘度（25℃，秒） Viscosity (25 ℃, seconds) | ≥90 | |
理论用量 Theoretical dosage | 150～200g/㎡ | |
配套用漆Matching paint | 面漆为醇酸磁漆、氨基烘漆等。 Topcoat is alkyd enamel, amino baking paint and so on. | |
表面处理Surface treatment | 被刷涂表面应干净、无水、无油污。 The surface to be brushed should be clean, water-free and oil-free. | |
施工参考Construction reference | 使用前应将漆液充分搅匀，用配套稀释剂稀释至施工粘度，可刷涂或者喷涂，涂覆后，如在 105℃下烘干，可使漆膜性能更好，底漆应干透才能涂面漆，避免被咬起。 The paint should be fully stirred before use, diluted to the construction viscosity with a matching diluent, and can be brushed or sprayed. After coating, the performance of the paint film can be better if it is dried at 105 ℃. The primer should be dry enough to apply the paint to avoid being bitten. | |
储藏期限 Storage period |
产品在规定储运条件下，漆料储存期为12 个月，超过储存期可按质量标准检验，如符合技术要求，仍可使用。Under the specified storage and transportation conditions, the storage period of paint is 12 months, which can be inspected according to the quality standard after the storage period. If it meets the technical requirements, it can still be used. | |
附注：本说明书有关数据是在标准条件下实验取得，实际使用时，因环境条件和施工方法的差异可能与之略有不同，以上数据如有改变，已本厂最新说明书为准，恕不另行通知。 Note: the relevant data in this manual are obtained by experiment under standard conditions. In actual use, they may be slightly different due to differences in environmental conditions and construction methods. If the above data are changed, the latest instructions of our factory will prevail without prior notice. | ||