主要组成 Main composition | 由酚醛漆料与防锈颜料及各色体质颜填料经研磨后加入催干剂调制而成。 It is made of phenolic paint, antirust pigment and various color pigments and fillers after grinding and adding drier. | |
主要特性Main characteristics | 自干型漆，漆膜干燥快、附着力防锈性能较好，易打磨。 Self-drying paint, fast drying of paint film, good adhesion and antirust performance, easy to polish. | |
主要用途Main use | 适于一般钢铁机械、设备表面作打底之用。 It is suitable for the surface of general iron and steel machinery and equipment. | |
基本参数 Basic parameters | 干燥时间（25±1℃），h Drying time (25 ±1 ℃), h | 表干≤2 Surface dry ≤ 2 |
干燥时间（25±1℃），h Drying time (25 ±1 ℃), h | 实干≤48 小时 Practical work ≤ 48 hours | |
硬度 Hardness | ≥0.3 | |
配套用漆 Matching paint | 各色酚醛调和漆、醇酸调和漆等。 Various colors of phenolic blending paint, alkyd blending paint, etc. | |
建议涂装道数 Recommended number of painting lines | 1 道 1 channel | |
复涂间隔时间 Interval time of recoating | 20～24 小时 20 to 24 hours | |
表面处理 Surface treatment | 被涂刷表面应无水、无油、无绣等，最好砂磨一道，提高表面清洁度和粗糙度，增强附着力。 The brushed surface should be free of water, oil, embroidery, etc., preferably sanded together to improve surface cleanliness and roughness and enhance adhesion. | |
施工参考Construction reference | 可刷涂或喷涂，使用前需将油漆充分搅匀，如粘度过大，用200#溶剂汽油或松节油兑稀，如有漆皮和粗颗粒，必须过滤方能使用，每道漆涂刷不能太厚，以免漆膜起皱或影响实干，需复涂几道时，要等前道漆膜干透后再涂下道漆。Can be brushed or sprayed, the paint should be fully stirred before use, such as excessive viscosity, diluted with 20g solvent gasoline or turpentine, if there are lacquer skins and coarse particles, must be filtered before use, each paint brush can not be too thick, lest the paint film wrinkles or affect the actual dry, need to reapply several times, wait for the previous paint film to dry before painting. | |
储藏期限 Storage period | 产品在规定储运条件下，漆料储存期为12 个月，超过储存期可按质量标准检验，如符合技术要求，仍可使用。Under the specified storage and transportation conditions, the storage period of paint is 12 months, which can be inspected according to the quality standard after the storage period. If it meets the technical requirements, it can still be used. | |
附注：本说明书有关数据是在标准条件下实验取得，实际使用时，因环境条件和施工方法的差异可能与之略有不同，以上数据如有改变，已本厂最新说明书为准，恕不另行通知。 Note: the relevant data in this manual are obtained by experiment under standard conditions. In actual use, they may be slightly different due to differences in environmental conditions and construction methods. If the above data are changed, the latest instructions of our factory will prevail without prior notice. | ||