主要组成 Main composition | 以自干型丙烯酸树脂（Ⅰ型）或热固丙烯酸树脂（Ⅱ型）为基料，加入颜料、改性树脂、助剂和有机溶剂配制而成。 It is prepared with self-drying acrylic resin (type Ⅰ) or thermosetting acrylic resin (type Ⅱ) as base material, adding pigments, modified resins, auxiliaries and organic solvents. | |
主要特性Main characteristics | Ⅰ型能在常温下干燥，漆膜光亮丰满，附着力好，并具有较好的保色保光性。 Type I can dry at room temperature, the paint film is bright and plump, has good adhesion, and has good color and gloss retention. Ⅱ型为烘干型，整体性能更好一些。 Type Ⅱ is drying type, and its overall performance is better. | |
主要用途Main use | Ⅰ型用于钢铁桥梁、大型机械。 Type I is used for iron and steel bridges and large machinery. Ⅱ型用于汽车、轻工、仪表、电器等工业产品及机电、玩具等金属表面作装饰保护涂料。 Type II is used as decorative and protective coatings for industrial products such as automobiles, light industry, instruments, electrical appliances and metal surfaces such as mechanical and electrical machinery and toys. | |
基本参数 Basic parameters |
干燥时间（25℃） Drying time (25 ℃). | Ⅰ型：表干：≤20min，实干：≤24h。 Type I: surface dry: ≤ 20min, practical: ≤ 24 h. |
Ⅱ型：浅色（110±5℃）≤30min，深色（120±5℃）≤30min Type Ⅱ: light color (1105C) ≤ 30min, dark color (1205C) ≤ 30min | ||
漆膜光泽 Paint film luster | Ⅰ型≥85%，Ⅱ型≥90%。 Type Ⅰ ≥ 85%, type Ⅱ ≥ 90%. | |
柔韧性：≤1 Flexibility ：≤ 1 | 附着力，级：≤1 Adhesion, grade: ≤ 1 | |
施工参考Construction reference | 该漆已喷涂为主，施工前必须将漆液搅拌均匀，如粘度过大，用配套的丙烯酸磁漆稀释剂或X-5 稀释剂稀释，施工粘度一般以15～20 秒（涂-4 粘度计，25±1℃）为宜，如有机械杂质应使用80 目以上滤网过滤后再喷涂。 The paint has been mainly sprayed, the paint must be stirred evenly before construction, such as excessive viscosity, diluted with matching acrylic enamel diluent or Xmur5 diluent, the construction viscosity is generally 15 seconds (coating-4 viscometer, 25 ±1 ℃), if there are mechanical impurities should be filtered with a filter of more than 80 mesh before spraying. | |
配 套 底 漆 Matching primer | 用于钢铁表面时以X06-1 磷化底漆或H06-2 铁红环氧酯底漆配套，用于铝金属表面时以X06-2 磷化底漆或H06-2 锌黄环氧酯底漆配套，不易用在不锈钢、镀锌铁和玻璃表面喷涂。 It is matched with X06-1 phosphating primer or H06-2 iron red epoxy ester primer when used on the surface of iron and steel, and X06-2 phosphating primer or H06-2 zinc yellow epoxy primer on aluminum metal surface, which is not easy to be sprayed on stainless steel, galvanized iron and glass surface. | |
建议涂装道数Recommended numberof painting lines | 保护性涂装要求一底两面或两底两面，干膜总厚度为80～110μm，要求不高时可采用一底一面施工，干膜总厚度为60～90μm。 Protective coating requires one bottom two sides or two bottom two sides, the total thickness of dry film is 80 ~ 110 μ m, when the requirement is not high, one bottom can be used, and the total thickness of dry film is 60 ~ 90 μ m. | |
储藏期限 Storage period | 产品在规定储运条件下，漆料储存期为12 个月，超过储存期可按质量标准检验，如符合技术要求，仍可使用。Under the specified storage and transportation conditions, the storage period of paint is 12 months, which can be inspected according to the quality standard after the storage period. If it meets the technical requirements, it can still be used. | |
附注：本说明书有关数据是在标准条件下实验取得，实际使用时，因环境条件和施工方法的差异可能与之略有不同，以上数据如有改变，已本厂最新说明书为准，恕不另行通知。 Note: the relevant data in this manual are obtained by experiment under standard conditions. In actual use, they may be slightly different due to differences in environmental conditions and construction methods. If the above data are changed, the latest instructions of our factory will prevail without prior notice. | ||