主要组成 Main composition | 由桐油及其他干性植物油和松香改性酚醛树脂、钙酯等经高温熬炼后，加入200#溶剂汽油或松节油及催干剂调配而成。 It is made of tung oil and other dry vegetable oils, rosin modified phenolic resin and calcium esters after high temperature refining and adding 20g solvent gasoline or turpentine and driers. | |
主要特性Main characteristics | 自干性漆，漆膜坚硬、耐油防潮性好，具有较高的表面电阻值，属 A 级绝缘材料。 Self-drying paint, paint film is hard, oil and moisture resistance is good, with high surface resistance, is a grade An insulation material. | |
主要用途Main use | 用于电器密封、装饰、涂刷硅钢片和低压使用件的外壳，也可作电器维修的使用。 It is used for sealing, decorating and brushing the shell of silicon steel sheet and low-voltage parts of electrical appliances. It can also be used for electrical maintenance. | |
基本参数 Basic parameters |
干燥时间（25℃） Drying time (25 ℃) | 表干：≤5 小时 Table dry: ≤ 5 hours |
实干：≤24 小时 Practical work: ≤ 24 hours | ||
击穿强度 KV/mm Breakdown strength KV/mm | 常态：≥30 Normal: ≥ 30 | |
浸水：≥30 Flooding: ≥ 30 | ||
表面处理Surface treatment |
被涂刷表面应无水、无油、无灰尘等。 The painted surface should be free of water, oil, dust, etc. | |
建议涂装道数Recommended numberof painting lines |
1～2 道 1-2 channels | |
复涂间隔时间 Interval time of recoating |
20～24 小时 20 to 24 hours | |
施工参考Construction reference | 多用浸涂，也可刷涂，如粘度过大，用200#溶剂汽油或松节油兑稀，每道漆涂刷不能太厚，以免漆膜起皱或影响实干，需复涂几道的，应等前道漆膜干透后再涂下道漆，低温潮湿天气，工件可以在50～60℃烘烤一小时左右。Multi-use immersion, can also be brushed, such as viscosity is too large, with 20 grams of solvent gasoline or turpentine mixed sparse, each paint brush can not be too thick, so as not to wrinkle the film or affect the actual dry, need to re-apply several, should wait for the front paint film dry and then apply the paint, low temperature and humid weather, the workpiece can be baked at 50 ℃ to 60 ℃ for an hour or so. | |
储藏期限 Storage period | 产品在规定储运条件下，漆料储存期为12 个月，超过储存期可按质量标准检验，如符合技术要求，仍可使用。Under the specified storage and transportation conditions, the storage period of paint is 12 months, which can be inspected according to the quality standard after the storage period. If it meets the technical requirements, it can still be used. | |
附注：本说明书有关数据是在标准条件下实验取得，实际使用时，因环境条件和施工方法的差异可能与之略有不同，以上数据如有改变，已本厂最新说明书为准，恕不另行通知。 Note: the relevant data in this manual are obtained by experiment under standard conditions. In actual use, they may be slightly different due to differences in environmental conditions and construction methods. If the above data are changed, the latest instructions of our factory will prevail without prior notice. | ||