主要组成 Main composition | 由环氧树脂、云母氧化铁、颜料、助剂等为主漆，以改性胺为固化剂，双组份包装。 It is mainly made of epoxy resin, mica iron oxide, pigments and auxiliaries, modified amine as curing agent, and two-component packaging. | |
主要特性Main characteristics | 在富锌底漆上或已处理的钢结构底材上具有良好的附着力，封闭性及耐磨性,与后道漆膜具有良好的层间附着力。 It has good adhesion, sealing and wear resistance on zinc-rich primer or treated steel structure substrate, and has good interlayer adhesion with rear paint film. | |
主要用途 Main use | 可作底漆,也可作为环氧富锌等防锈漆的中间涂层,以增加整个涂层的保护性能。 It can be used as a primer or as an intermediate coating of epoxy zinc-rich antirust paint to increase the protective performance of the whole coating. | |
基本参数 Basic parameters | 干燥时间（25℃） Drying time (25 ℃) | 表干：≤4 小时，实干：≤24 小时。 Table dry: ≤ 4 hours, practical work: ≤ 24 hours. |
表面处理 Surface treatment | 施工前应对工件表面进行清洁处理，除锈等级st3 或Sa2.5 以上，若基面有油污，应先除油（稀释剂擦洗等方法）。 The surface of the workpiece should be cleaned before construction, and the rust removal grade is above st3 or Sa2.5. If there is oil on the base surface, the oil should be removed first (diluent scrub, etc.). | |
注意事项 Matters needing attention | 1、双组份漆，用多少配多少，避免干固浪费,配好的油漆应在 3 小时内用完； 1, two-component paint, how much to use, to avoid dry solid waste, the prepared paint should be used up within 3 hours. 2、为保持涂层最终效果和促使涂层干燥，在施工过程中和结束后，必须保持良好通风； 2. In order to maintain the final effect of the coating and make the coating dry, good ventilation must be maintained during and after construction. 3、施工工具和环境应保持清洁干燥。 3. Construction tools and environment should be kept clean and dry. 用剩固化剂要注意密封盖严，否则会固化报废。 When using the residual curing agent, we should pay attention to the tight sealing, otherwise it will be solidified and scrapped. 4、 施工结束时，所有器具立即用溶剂冲洗，以防干固； 4. at the end of the construction, all utensils should be washed with solvent immediately to prevent drying and consolidation. 5、施工时穿戴好防护用品，避免吸入漆雾，涂料溅在皮肤上应立即用合适的清洁剂和肥皂清洗，如溅入眼睛，请及时用水冲洗并就医。 5. Wear protective equipment during construction to avoid inhaling paint fog. paint splashing on the skin should be washed immediately with appropriate detergent and soap. If splashed into the eyes, rinse with water and see a doctor in time. | |
施工参考Construction reference | 1、推荐采用空气喷涂，以获得均匀良好的涂膜，也可采用辊涂或刷涂方法施工； 1. Air spraying is recommended to obtain uniform and good film, and roller coating or brush coating can also be used. 2、主漆应充分搅拌均匀，以防止局部色差，按规定比例将主漆、固化剂混合后，静置10～15 分钟再喷涂，每道施工间隔（23±2℃）12～24h（配漆和涂装过程中，严禁与水、酸、碱等接触），对超过涂装间隔的底层涂层，推荐使用800 目（底漆）以上砂纸整体打磨处理，才能涂面漆， 2. The main paint should be fully stirred evenly to prevent local color difference. After mixing the main paint and curing agent according to the prescribed proportion, rest for 10 minutes and 15 minutes before spraying, with each construction interval (23 ±2 ℃) 12 minutes 24 hours (contact with water, acid, alkali, etc.). Contact with water, acid, alkali, etc.). For the bottom coating that exceeds the coating interval, it is recommended to use sandpaper with more than 800 mesh (primer) before painting. 否则会影响层间附着力； Otherwise, the interlayer adhesion will be affected. 3、在施工过程中，为防止有意外粗颗粒或机械杂质混入，必须使用 80 目以上滤网进行过滤。 3. In the process of construction, in order to prevent the mixing of accidental coarse particles or mechanical impurities, more than 80 mesh filter must be used for filtration. 如需降粘度，用配套稀释剂调稀（不能使用汽油松节油二甲苯类等单一溶剂稀释，否则会影响施工质量，甚至造成报废）； If you need to reduce viscosity, use matching diluents to adjust thinning (you can not use gasoline, turpentine, xylene and other single solvent dilution, otherwise it will affect the construction quality and even lead to scrap). 4、施工温度≥10℃，相对湿度≤85%，特殊环境要求，可与厂家联系，按特殊情况对产品进行专门调配。 4. Construction temperature ≥ 10 ℃, relative humidity ≤ 85%, special environmental requirements, you can contact the manufacturer and specially deploy the products according to the special circumstances. | |
储藏期限 Storage period | 产品在规定储运条件下，有效贮存期为固化剂6 个月，漆液12 个月，超过储存期可按质量标准检验，如符合技术要求，仍可使用。 Under the specified storage and transportation conditions, the effective storage life of the product is 6 months for curing agent and 12 months for paint liquid. If the storage period exceeds the storage period, it can be tested according to the quality standard. If it meets the technical requirements, it can still be used. | |
附注：本说明书有关数据是在标准条件下实验取得，实际使用时，因环境条件和施工方法的差异可能与之略有不同，以上数据如有改变，已本厂最新说明书为准，恕不另行通知。 Note: the relevant data in this manual are obtained by experiment under standard conditions. In actual use, they may be slightly different due to differences in environmental conditions and construction methods. If the above data are changed, the latest instructions of our factory will prevail without prior notice. | ||